Method of manufacturing a semiconductor device and a semiconductor device

ABSTRACT

A method of manufacturing a semiconductor device, has forming a gate insulating film over a surface of a substrate, eliminating a portion of the gate insulating film in a region, forming a gate electrode over the gate insulating film and a drain electrode on the region, implanting first impurities into the substrate using the gate electrode and the drain electrode as a mask, forming an insulating film to fill the space between the gate electrode and the drain electrode, and implanting second impurities into the substrate to form a source region using the gate electrode, the drain electrode and the insulating film as a mask.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a Divisional of application Ser. No. 12/054,684,filed Mar. 25, 2008, which claims priority of Japan Patent Application2007-080159, filed Mar. 26, 2007, the entire disclosures of which arehereby incorporated by reference.

TECHNICAL FIELD

This technical field relates to a method of manufacturing a highbreakdown-voltage semiconductor device and a structure of a highbreakdown-voltage semiconductor device.

BACKGROUND

High breakdown-voltage semiconductor devices are expected to haveexcellent radio-frequency characteristics and high breakdown voltage ofsource/drain regions.

In such a high breakdown-voltage semiconductor device, when a voltagehigher than a certain level is applied to a drain region, a largeelectric field occurs at the boundary between the drain region and achannel region, and junction breakdown occurs at the boundary.Therefore, a problem in increasing breakdown voltage is how to reduce anelectric field produced at the boundary between the drain region and thechannel region.

SUMMARY

A method of manufacturing a semiconductor device, has forming a gateinsulating film over a surface of a substrate, eliminating a portion ofthe gate insulating film in a region, forming a gate electrode over thegate insulating film and a drain electrode on the region, implantingfirst impurities into the substrate using the gate electrode and thedrain electrode as a mask, forming an insulating film to fill the spacebetween the gate electrode and the drain electrode, and implantingsecond impurities into the substrate to form a source region using thegate electrode, the drain electrode and the insulating film as a mask.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A is a plan view of a high breakdown-voltage semiconductor deviceaccording to a first embodiment;

FIG. 1B is a schematic sectional view of a principal portion of the highbreakdown-voltage semiconductor device according to the firstembodiment;

FIGS. 2A to 2D are schematic sectional views each showing a principalportion in a step for manufacturing the high breakdown-voltagesemiconductor device according to the first embodiment;

FIGS. 3A to 3D are schematic sectional views each showing a principalportion in a step for manufacturing the high breakdown-voltagesemiconductor device according to the first embodiment;

FIGS. 4A to 4C are schematic sectional views each showing a principalportion in a step for manufacturing the high breakdown-voltagesemiconductor device according to the first embodiment;

FIG. 5 is a graph showing changes of the voltage between source anddrain regions of the high breakdown-voltage semiconductor deviceaccording to the first embodiment;

FIG. 6A is a plan view of a high breakdown-voltage semiconductor deviceaccording to a second embodiment; and

FIG. 6B is a schematic sectional view of a principal portion of the highbreakdown-voltage semiconductor device according to the secondembodiment.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

A method of manufacturing a high breakdown-voltage semiconductor deviceand a structure of a high breakdown-voltage semiconductor device aredescribed with reference to embodiments. However, the followingembodiments are not limited to these embodiments.

First Embodiment

An n-type high breakdown-voltage semiconductor device and a method ofmanufacturing an n-type high breakdown-voltage semiconductor deviceaccording to a first embodiment are described in detail with referenceto FIGS. 1A and 1B. The semiconductor device and the method ofmanufacturing the semiconductor device according to the first embodimentare characterized in that a LDD region is formed in a self alignmentmanner with a gate electrode and a drain electrode.

FIGS. 1A and 1B are drawings each showing a principal portion of asemiconductor device according to the first embodiment.

FIG. 1A is a plan view of a high breakdown-voltage semiconductor deviceaccording to the first embodiment. FIG. 1A shows a highbreakdown-voltage semiconductor device 100 including a gate electrode 4a, a drain electrode 6 a, an insulating film 7 a constituting a firstsidewall spacer, an insulating film 7 b constituting a second sidewallspacer, a source region 8 a, contact plugs 20 a for connecting wiring tothe source region, contact plugs 20 b for connecting wiring to the drainregion, and a contact plug 20 c for connecting wiring to the gateelectrode 4 a. Also, a silicide layer 9 and an interlayer insulatingfilm are formed on the surfaces of the gate electrode 4 a, the drainelectrode 6 a, and the source region 8 a.

The gate electrode 4 a, the drain electrode 6 a, and the source region 8a are formed by implanting a high concentration of conductive impuritiesinto silicon. Specifically, phosphorus ions are implanted into the gateelectrode 4 a, the drain electrode 6 a, and the source region 8 a at aphosphorus concentration of, for example, 5.0×10²⁰ cm⁻³. The insulatingfilm 7 a constituting the first sidewall spacer and the insulating film7 b constituting the second sidewall spacer are insulative and arecomposed of, for example, silicon oxide. The contact plugs 20 a forconnecting wiring to the source region 8 a, the contact plugs 20 b forconnecting wiring to the drain electrode 6 a, and the contact plug 20 cfor connecting wiring to the gate electrode 4 a are composed of tungstenand are electrically connected to the source region 8 a, the drainelectrode 6 a, and the gate electrode 4 a, respectively.

As shown in FIG. 1A, the drain electrode 6 a is formed on one of thesides of the gate electrode 4 a on a substrate. The source region 8 a isformed on the other side of the gate electrode 4 a within the substrate.The insulating film 7 a constituting the first sidewall spacer and theinsulating film 7 b constituting the second sidewall spacer are formedaround the gate electrode 4 a and the drain electrode 6 a. Further, anelement separation region 12 is formed around the high breakdown-voltagesemiconductor device 100.

FIG. 1B is a schematic sectional view showing a principal portion of afirst example of the high breakdown-voltage semiconductor deviceaccording to the first embodiment. FIG. 1B is a sectional view of thehigh breakdown-voltage semiconductor device 100, taken along line X-X′in FIG. 1A. The high breakdown-voltage semiconductor device 100 includesa p-type silicon substrate 1, a p-type well region 2 a, a gateinsulating film 3, the gate electrode 4 a, a n-type drain region 5 a,the drain electrode 6 a, the insulating film 7 a constituting the firstsidewall spacer, the insulating film 7 b constituting the secondsidewall spacer, the n-type source region 8 a, the cobalt silicide layer9, and the element separation region 12. In FIG. 1B, the completely samecomponents as in FIG. 1A are denoted by the same reference numerals.

The substrate 1 is a p-type silicon substrate having a p-type impurityconcentration of, for example, 1.0×10¹⁵ cm⁻³. The element separationregion 12 has a shallow trench isolation structure. The p-type wellregion 2 a is formed by implanting boron ions into the substrate 1. Thep-type well region 2 a has a boron concentration of, for example,1.0×10¹⁶ cm⁻³ and a depth of 350 nm. The gate insulating film 3 iscomposed of silicon oxide and formed over the substrate 1. The thicknessof the gate insulating film 3 is, for example, 6 nm. The gate electrode4 a is formed over the surface of the gate insulating film 3, and thedrain region 5 a is formed on one of the sides of the gate electrode 4 awithin the substrate 1. The drain region 5 a is doped with phosphorusions implanted as n-type conductive impurities at a low concentration. Aregion in which a low concentration of conductive impurities is diffusedis referred to as a “Lightly Doped Drain (LDD) region”. The drain region5 a has a phosphorus concentration of 1.0×10¹⁹ cm⁻³ and a depth of 50nm. The drain electrode 6 a is connected to the drain region 5 a and animpurity diffusion layer 6 b is formed by inwardly diffusing firstimpurities or second impurities, which are implanted into the drainelectrode 6 a, from the surface of the substrate 1. The insulating film7 a constituting the first sidewall spacer is formed on the sourceregion-side sidewall of the gate electrode 4 a. The insulating film 7 bconstituting the second sidewall spacer is formed on the drain-sidesidewall of the gate electrode 4 a to fill the space between the drainelectrode 6 a and the gate electrode 4 a. The source region 8 a isformed on the other side of the gate electrode 4 a within the substrate1. The silicide layer 9 is composed of low-resistance phase cobaltsilicide. The silicide layer 9 is formed on the surfaces of the sourceregion 8 a, the gate electrode 4 a, and the drain electrode 6 a.

A process for manufacturing the high breakdown-voltage semiconductordevice according to the first embodiment is described with reference toFIGS. 2A to 2D, 3A to 3D, and 4A to 4C.

FIG. 2A is a schematic sectional view of a principal portion in the stepof preparing the substrate. FIG. 2A shows the substrate 1, the p-typewell region 2 a, and the element separation region 12. The substrate 1is a p-type silicon substrate having a p-type impurity concentration of,for example, 1.0×10¹⁵ cm⁻³. The element separation region 12 has ashallow trench isolation structure and is formed by implanting boronions into the substrate 1. The p-type well region 2 a has a boronconcentration of, for example, 1.0×10¹⁶ cm⁻³ and a depth of 350 nm.

FIG. 2B is a schematic sectional view showing the principal portion inthe step of forming the gate insulating film 3 over the surface of thesubstrate. FIG. 2B shows the gate insulating film 3 in addition to FIG.2A. The gate insulating film 3 is composed of silicon oxide.

As shown in FIG. 2B, the surface of the substrate 1 is thermallyoxidized to form the gate insulating film 3 having a thickness of, forexample, 6 nm on the surface of the substrate 1.

FIG. 2C is an enlarged sectional view showing the principal portion inthe step of eliminating (etching out) a portion with a width of about300 nm from the gate insulating film 3 in a region where the drainelectrode is to be formed.

FIG. 2D is an enlarged sectional view showing the principal portion inthe step of depositing polysilicon 16 over the surfaces of the substrate1 and the gate insulating film 3. FIG. 2D shows the polysilicon 16 inaddition to FIG. 2C.

FIG. 3A is an enlarged schematic view showing the principal portion inthe step of simultaneously forming the gate electrode over the gateinsulating film and the drain electrode on the drain region with a spacetherebetween. FIG. 3A shows the gate electrode 4 a and the drainelectrode 6 a in addition to FIG. 2D. The width of each of the gateelectrode 4 a and the drain electrode 6 a is 300 nm.

As shown in FIG. 3A, the polysilicon 16 is patterned by photolithographyto form the gate electrode 4 a and the drain electrode 6 a. The distancebetween the gate electrode 4 a and the drain electrode 6 a ispreferably, for example, 0.2 μm to 0.3 μm. This is because theinsulating film 7 b constituting the second sidewall spacer fill thespace between the gate electrode 4 a and the drain electrode 6 a asdescribed below.

FIG. 3B is an enlarged schematic view showing the principal portion inthe step of implanting first impurities as low-concentration conductiveimpurities into the space between the gate electrode 4 a and the drainelectrode 6 a. FIG. 3B shows low-concentration impurity regions 17subsequent to FIG. 3A. In the substrate 1, the low-concentrationimpurity regions 17 have a phosphorus concentration of 1.0×10¹⁹ cm⁻³ anda depth of 50 nm. In this embodiment, the first impurities arephosphorus.

As shown in FIG. 3B, phosphorus is implanted as n-type conductiveimpurities at a low concentration into the drain region 5 a from thespace between the gate electrode 4 a and the plug 6 a using the gateelectrode 4 a and the drain electrode 6 a as a mask to form thelow-concentration impurity regions 17.

FIGS. 3C and 3D are enlarged schematic views each showing the principalportion in the step forming the insulating film 18 to fill the space.FIG. 3C shows the insulating film 18 in addition to FIG. 3B. Theinsulating film is composed of, for example, silicon oxide.

As shown in FIG. 3C, the insulating film 18 is thickly deposited on thesurfaces of the gate electrode 4 a, the plug 6 a, and the spacetherebetween so as to completely fill the space.

FIG. 3D shows the insulating film 7 a constituting the first sidewallspacer and the insulating film 7 b constituting the second sidewallspacer in addition to FIG. 3C. The insulating films 7 a and 7 b arecomposed of, for example, silicon oxide.

As shown in FIG. 3D, anisotropic etching is performed to simultaneouslyform the insulating film 7 a constituting the first sidewall spacer onthe sidewall on the source region side of the gate electrode 4 a and theinsulating film 7 b constituting the second sidewall spacer on thesidewall on the drain side of the gate electrode 4 a. In this step, thespace between the gate electrode 4 a and the drain electrode 6 a isfilled with the insulating film 7 b constituting the second sidewallspacer.

FIG. 4A is an enlarged schematic view showing the principal portion inthe step of implanting a high-concentration of conductive impurities assecond impurities into the source region, the gate electrode, and thedrain electrode. FIG. 4A shows the source region 8 a in addition to FIG.3D. As shown in FIG. 4A, phosphorus ions as conductive impurities at ahigh concentration are implanted as the second impurities using the gateelectrode 4 a, the plug 6 a, the insulating film 7 a constituting thefirst sidewall spacer, and the insulating film 7 b constituting thesecond sidewall spacer as a mask to form the n-type source region 8 ahaving a phosphorus concentration of, for example, 5.0×10²⁰ cm⁻³ and adepth of 100 nm.

FIG. 4B is an enlarged schematic view showing the principal portion inthe step of activating the first or second impurities implanted into thedrain electrode 6 a and diffusing the first or second impurities fromthe drain electrode 6 a into the substrate by heat treatment. In thisstep, the impurity diffusion layer 6 b connected to the shallow drainregion 5 a is formed below the drain electrode 6 a. FIG. 4B shows thedrain region 5 a in addition to FIG. 4A. As shown in FIG. 4B, the firstor second impurities implanted in the previous step are activated by anactivation annealing treatment. At the same time, the first or secondimpurities diffuse inward from the surface of the substrate 1 to formthe impurity diffusion layer 6 b.

FIG. 4C is an enlarged schematic view showing the principal portion inthe step of forming the silicide layer on the surfaces of the sourceregion, the gate electrode, and the drain electrode. FIG. 4C shows thecobalt silicide layer 9 in addition to FIG. 4B.

As shown in FIG. 4C, a metal film, e.g., a cobalt film, is deposited onthe surface of the substrate 1, including the surfaces of the sourceregion 8 a, the gate electrode 4 a, and the drain electrode 6 a,followed by heat treatment to form the cobalt silicide layer 9 as ametal silicide on the surfaces of the source region 8 a, the gateelectrode 4 a, and the drain electrode 6 a. Then, the unreacted cobaltfilm is removed, and then the cobalt silicide layer 9 is converted tolow-resistance phase cobalt silicide by a second heat treatment.

Then, the steps of forming the contact plugs 20 a to 20 c shown in FIG.1A and forming an interlayer insulating film and wiring are performed tocomplete the high breakdown-voltage semiconductor device 100 accordingto this embodiment.

FIG. 5 shows changes of the voltage between the source and drain regionsof the high breakdown-voltage semiconductor device according to thefirst embodiment. In FIG. 5, the depth [μm] of the drain region 5 a isshown as abscissa, and the voltage [V] applied to the gate end when avoltage of 10 V is applied between the source 8 a and the drainelectrode 6 a is shown as ordinate. In the figure, OFFSET represents thedistance [μm] between the gate electrode 4 a and the drain electrode 6a. Further, a dotted line shows changes of the voltage when the distancebetween the gate electrode 4 a and the drain electrode 6 a is 0.1 [μm],and a solid line shows changes of the voltage when the distance betweenthe gate electrode 4 a and the drain electrode 6 a is 0.2 [μm]. Theother lines show changes of the voltage when the distance between thegate electrode 4 a and the drain electrode 6 a is 0.3 [μm] or more.

FIG. 5 shows that when the distance between the gate electrode 4 a andthe drain electrode 6 a is 0.3 [μm] or more, the maximum value of thevoltage applied to the gate end is about 3.7 [V]. In a highbreakdown-voltage semiconductor device, the length of the LDD region 5 ais generally increased for reducing the electric field at the gate end.However, FIG. 5 indicates that the effect of reducing the electric fieldcannot be obtained even when the distance between the gate electrode 4 aand the drain electrode 6 a is set to 0.3 [μm] or more. Also, it isdesired that the distance between the gate electrode 4 a and the drainelectrode 6 a is such narrow that it is filled with the insulating film7 a constituting the first sidewall spacer and the insulating film 7 bconstituting the second sidewall spacer.

Further, in the high breakdown-voltage semiconductor device, thedistance between the gate electrode 4 a and the drain electrode 6 a isdetermined in consideration of not only the optimum value but alsoon-resistance having a trade-off relation to breakdown voltage.Therefore, the distance between the gate electrode 4 a and the drainelectrode 6 a can be set to 0.2 [μm] or less. In this case, the distancebetween the gate electrode 4 a and the drain electrode 6 a can be filledby depositing, to 0.1 μm, the insulating film 7 a constituting the firstsidewall spacer and the insulating film 7 b constituting the secondsidewall spacer.

In the above-mentioned structure of the high breakdown-voltagesemiconductor device, a LDD region is formed between the gate electrode4 a and the drain electrode 6 a, and thus the electric field applied tothe boundary between the drain region 5 a and the channel region can bereduced. As a result, the breakdown voltage between the drain region 5 aand the substrate 1 can be increased.

The impurity diffusion region 6 b is a drain region. The drain regionshallower than the source region can be formed in a self alignmentmanner by the step of implanting a low concentration of conductiveimpurities into the space between the drain electrode 6 a and the gateelectrode 4 a and the step of diffusing the conductive impurities fromthe drain electrode 6 a into the substrate by a heat treatment.Therefore, unlike in a case in which the LDD region is formed using amask, alignment is unnecessary, thereby improving variations in thecharacteristics of the semiconductor device and permitting a reductionof the gate length.

In addition, since the drain electrode 6 a and the gate electrode 4 aare formed by the same step using the mask, an alignment marginnecessary for combining a plurality of mask steps become unnecessarywhen the distance between the drain electrode 6 a and the gate electrode4 a is determined. Therefore, the distance between the gate electrode 4a and the drain electrode 6 a can be securely set to an optimum valuedetermined by a trade-off relation between the parasitic resistance andelectric field reduction in the drain region 5 a.

Further, although the high breakdown-voltage semiconductor devicedescribed in this embodiment is a n-type semiconductor device, thetransistor may be a p-type high breakdown-voltage semiconductor device.In this case, the conductivity type in the above-described n-type highbreakdown-voltage semiconductor device may be reversed.

In addition, this embodiment is not limited to the constitution andconditions described in the embodiment, and various changes can be made.For example, the impurity concentrations, depths, thicknesses, gatelength, and distance length, which are described in the firstembodiment, are only examples, and these values may be appropriatelydetermined according to the required high breakdown voltage andhigh-frequency characteristics.

Further, the insulating film that fills the space between the gateelectrode and the drain electrode serves as a silicide block. Therefore,the insulating film exhibits high compatibility with a CMOS logicprocess, and thus a high breakdown-voltage transistor can bemanufactured without additional steps, thereby realizing integration ofa power amplifier using the high breakdown-voltage transistor and acontrol logic circuit at a low cost.

For example, when the high breakdown-voltage transistor is used for ahigh-frequency power amplifier, the transistor is frequently mixed witha control CMOS logic circuit. When a RF circuit and a base band circuitare mounted on a chip in future, of course, mixing with CMOS isrequired. Therefore, the manufacturing method which has highcompatibility with a logic CMOS process is preferred.

Second Embodiment

A high breakdown-voltage semiconductor device according to a secondembodiment is described in detail with reference to FIGS. 6A and 6B. Inthe high breakdown-voltage transistor according to the secondembodiment, a gate electrode is formed to surround a drain region, andthus the area of the drain region can be decreased, thereby reducing theparasitic capacitance of the drain region.

FIG. 6A is a plan view of a high breakdown-voltage semiconductor deviceaccording to the second embodiment. FIG. 6A shows a highbreakdown-voltage Semiconductor device 110 including a gate electrode 4a, a drain electrode 6 a, an insulating film 7 a constituting a firstsidewall spacer, an insulating film 7 b constituting a second sidewallspacer, a source region 8 a, contact plugs 20 a for connecting wiring tothe source region, contact plugs 20 b for connecting wiring to the drainelectrode, and a contact plug 20 c for connecting wiring to the gateelectrode 4 a. Also, a silicide layer 9 and an interlayer insulatingfilm are formed on the surfaces of the gate electrode 4 a, the drainelectrode 6 a, and the source region 8 a. In FIG. 6A, the completelysame components as those shown in FIG. 1A are denoted by the samereference numerals. As shown in FIG. 6A, the gate electrode 4 a isformed to surround the drain electrode 6 a.

FIG. 6B is a schematic sectional view of a principal portion of the highbreakdown-voltage semiconductor device according to the secondembodiment, taken along line X-X′ in FIG. 6A. FIG. 6B shows the highbreakdown-voltage semiconductor device 110 including a substrate 1, ap-type well region 2, a gate insulating film 3, the gate electrode 4 a,a drain region 5 a, the drain electrode 6 a, an impurity diffusion layer6 b, the insulating film 7 a constituting the first sidewall spacer, theinsulating film 7 b constituting the second sidewall spacer, the sourceregion 8 a, the cobalt silicide layer 9, and an element separationregion 12. In FIG. 6B, the completely same components as in FIG. 6A aredenoted by the same reference numerals.

The high breakdown-voltage semiconductor device according to the secondembodiment has the structural characteristic that the gate electrode 4 ais formed to surround the drain region 5 a and the drain electrode 6 a.In this constitution, the number of portions, for example edge region(edges) where an electric field is concentrated between the gateelectrode 4 a and the drain region 5 a is inevitably decreased. Also,the area of the drain region 5 a can be decreased, and thus theparasitic capacitance of the drain region can be decreased. As a result,reduction of the electric field in the drain region 5 a can be furtherimproved.

Typical examples of application include a high-frequency power amplifierused in a transmission portion of a mobile communication apparatus suchhas a cellular phone. However, the present embodiment can be used inother applications in which high breakdown voltage and high-frequencycharacteristics are required.

What is claimed is:
 1. A semiconductor device comprising: a gateinsulating film formed over a substrate; a gate electrode over the gateinsulating film; a drain region formed within the substrate on one sideof the gate electrode; a drain electrode formed on the substrate andelectrically connected to the drain region, the drain electrode is apolysilicon implanted with conductive impurities; a first silicide layeron the surface of the drain electrode; a sidewall insulating film formedon the side of the gate electrode opposite to the drain electrode; aninsulating film formed between the gate electrode and the drainelectrode; and a source region having a grater depth than the drainregion and being formed adjacent to the sidewall insulating film,wherein the drain region is aligned to the gate electrode and the drainelectrode.
 2. The semiconductor device according to claim 1, furthercomprising: second silicide layers formed on the source region and thegate electrode.
 3. The semiconductor device according to claim 1,wherein the gate electrode is formed to surround the drain electrode. 4.A semiconductor device comprising: a gate insulating film formed over asubstrate; a gate electrode over the gate insulating film; a drainregion formed within the substrate on one side of the gate electrode; adrain electrode formed on the substrate and electrically connected tothe drain region, the drain electrode is a polysilicon implanted withconductive impurities; a first silicide layer on the surface of thedrain electrode; a sidewall insulating film formed on the side of thegate electrode opposite to the drain electrode; an insulating filmformed between the gate electrode and the drain electrode; and a sourceregion having a grater depth than the drain region and being formedadjacent to the sidewall insulating film, wherein implanting impuritiesinto the substrate to form a source region using the gate electrode, thedrain electrode and the insulating film as a mask.
 5. The semiconductordevice according to claim 4, further comprising: second silicide layersformed on the source region and the gate electrode.
 6. The semiconductordevice according to claim 4, wherein the gate electrode is formed tosurround the drain electrode.